LNP STAT-KON* POLYAMIDES COMPOUND
TOUGH, TAILORED ELECTRICAL PROPERTIES
Polyamide-based LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.
LNP™ STAT-KON™ Compound PA610 QD000I 塑料数据物性表
Also known as:LNP™ Stat-kon™ Compound Q-HI
Product reorder name:QD000I
LNP* Stat-kon* QD000I is a compound based on Nylon 6/10 resin containing Carbon Powder, Impact Modifier. Added features of this material include: Electrically Conductive, High Impact.
MECHANICAL | Value | Unit | Standard |
Tensile Stress,break | 320 | kgf/cm² | ASTM D 638 |
Tensile Strain,break | 52.7 | % | ASTM D 638 |
Flexural Stress | 550 | kgf/cm² | ASTM D 790 |
Flexural Modulus | 17500 | kgf/cm² | ASTM D 790 |
IMPACT | Value | Unit | Standard |
Izod Impact,notched,23℃ | 61 | cm-kgf/cm | ASTM D 256 |
THERMAL | Value | Unit | Standard |
HDT,1.82 MPa,3.2mm,unannealed | 55 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 1.17E-04 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,xflow | 1.17E-04 | 1/℃ | ASTM E 831 |
PHYSICAL | Value | Unit | Standard |
Density | 1.11 | g/cm³ | ASTM D 792 |
Moisture Absorption,50% RH,24 hrs | 0.28 | % | ASTM D 570 |
Mold Shrinkage,flow,24 hrs(5) | 0.1-0.3 | % | ASTM D 955 |
Mold Shrinkage,xflow,24 hrs(5) | 0.2-0.4 | % | ASTM D 955 |
Mold Shrinkage,flow,24 hrs(5) | 1-3 | % | ISO 294 |
Mold Shrinkage,xflow,24 hrs(5) | 1-3 | % | ISO 294 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | 1.E+02-1.E+04 | Ohm-cm | ASTM D 257 |
Surface Resistivity | 1.E+02-1.E+04 | Ohm | ASTM D 257 |
Source GMD,last updated:2004/10/01 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 80 | ℃ |
Drying Time | 4 | hrs |
Maximum Moisture Content | 0.12-0.2 | % |
Melt Temperature | 270-275 | ℃ |
Front-Zone 3 Temperature | 270-280 | ℃ |
Middle-Zone 2 Temperature | 260-270 | ℃ |
Rear-Zone 1 Temperature | 250-260 | ℃ |
Mold Temperature | 80-95 | ℃ |
Back Pressure | 0.2-0.3 | MPa |
Screw Speed | 30-60 | rpm |
Source GMD,last updated:2004/10/01 |