PA610 QFP36 含玻璃纤维,硅胶,聚四氟乙烯,内部润滑
  • 产 品:PA610 QFP36 含玻璃纤维,硅胶,聚四氟乙烯,内部润滑
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP Lubricomp* Polyamides Compound
Enhanced wear resistance, lower friction in tough
Polyamide-based LNP Lubricomp compounds provide these tough resins with improved wear resistance and lower friction by combining them with internal lubricants. Glass and carbon fibers can also be included for improved strength and stiffness.

LNP™ Lubricomp™ Compound PA610 QFP36 塑料物性

Also known as:LNP™ Lubricomp™ Compound QFL-4536
Product reorder name:QFP36
LNP LUBRICOMP* QFP36 is a compound based on Nylon 6/10 resin containing Glass Fiber, Silicone, PTFE. Added features of this material include: Internally Lubricated.

MECHANICAL Value Unit Standard
Tensile Stress,break 1390 kgf/cm² ASTM D 638
Tensile Strain,break 2.8 % ASTM D 638
Flexural Stress 2160 kgf/cm² ASTM D 790
Flexural Modulus 87800 kgf/cm² ASTM D 790
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 92 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 9 cm-kgf/cm ASTM D 256
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 201 ASTM D 648
PHYSICAL Value Unit Standard
Density 1.44 g/cm³ ASTM D 792
Mold Shrinkage,flow,24 hrs(5) 0.2 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.9 % ASTM D 955
Source GMD,last updated:2004/09/30
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.12-0.2 %
Melt Temperature 270-275
Front-Zone 3 Temperature 270-280
Middle-Zone 2 Temperature 260-270
Rear-Zone 1 Temperature 250-260
Mold Temperature 80-95
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD, last updated:2004/09/30

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.