快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：PA6 PFD06 含玻璃纤维和碳粉,导电尼龙6
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP™ STAT-KON™ Compound PA6 PFD06
Also known as:LNP™ Stat-kon™ Compound PF-30 Product reorder name:PFD06
LNP* Stat-kon* PFD06 is a compound based on Nylon 6 resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,break | 1620 | kgf/cm² | ASTM D 638 |
| Tensile Strain,break | 2.3 | % | ASTM D 638 |
| Tensile Modulus,50 mm/min | 119500 | kgf/cm² | ASTM D 638 |
| Flexural Stress | 2460 | kgf/cm² | ASTM D 790 |
| Flexural Modulus | 112400 | kgf/cm² | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 92 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 10 | cm-kgf/cm | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT,1.82 MPa,3.2mm,unannealed | 206 | ℃ | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.43 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.5 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 0.4 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 1.2 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 0.38 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 1.15 | % | ISO 294 |
| Moisture Absorption(23℃/50% RH) | 0.91 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.00E+03 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+00-6.E+00 | Ohm | ASTM D 257 |
| Source GMD,last updated:2005/08/02 | |||
| parameter lnjection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15-0.25 | % |
| Melt Temperature | 265-275 | ℃ |
| Front-Zone 3 Temperature | 275-290 | ℃ |
| Middle-Zone 2 Temperature | 265-275 | ℃ |
| Rear-Zone 1 Temperature | 250-260 | ℃ |
| Mold Temperature | 80-95 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD, last updated:2005/08/02 | ||