快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：PA6 PFD04 含有玻璃纤维和碳粉.导电尼龙6
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP™ STAT-KON™ Compound PA6 PFD04 塑料物性表
LNP* Stat-Kon* PFD04 is a compound based on PA6 containing Glass Fiber and Carbon Powder. Characteristics of this grade are Electrically Conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yield,5mm/min | 107 | MPa | ISO 527 |
| Tensile Stress,break,5mm/min | 87 | MPa | ISO 527 |
| Tensile Strain,break,5mm/min | 2.6 | % | ISO 527 |
| Tensile Modulus,1mm/min | 7000 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 152 | MPa | ISO 178 |
| Flexural Stress,break,2mm/min | 136 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 5900 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched 80*10*4 +23℃ | 50 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 11 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE,23℃ to 60℃,flow | 3.50E-05 | 1/℃ | ISO 11359-2 |
| CTE,23℃ to 60℃,xflow | 1.12E-04 | 1/℃ | ISO 11359-2 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 214 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 195 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar,flow(2)(5) | 0.4-0.6 | % | SABIC Method |
| Density | 1.32 | g/cm³ | ISO 1183 |
| Water Absorption,23℃/24hrs | 1 | % | ISO 62-1 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 4.E+00-6.E+00 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant,94HB Flame Class Rating(3)(4) | 1 | mm | UL 94 by SABIC-IP |
| Source GMD,last updated:2010/08/24 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15-0.25 | % |
| Melt Temperature | 265-275 | ℃ |
| Front-Zone 3 Temperature | 275-290 | ℃ |
| Middle-Zone 2 Temperature | 265-275 | ℃ |
| Rear-Zone 1 Temperature | 250-260 | ℃ |
| Mold Temperature | 80-95 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2010/08/24 | ||