- 产 品：PA6 PX08322 导热矿物填充阻燃尼龙6
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP* Konduit* Compound
LNP Konduit Resin All Series
LNP* Konduit* composite compounds are 10 to 50 times more thermally conductive than conventional unfilled thermoplastics. Konduit composite compounds can conduct heat away from devices into a heat sink or the surrounding air. LNP* specialty compound offerings are available in a broad portfolio of standard and engineering materials
LNP™ Konduit™ Compound PA6 PX08322 塑料物性
Also known as:LNP™Konduit™Compound PX08322
Product reorder name:PX08322
Thermally conductive mineral filled PA6 FR compound, with through-plane and in-plane thermal conductivity of 2.1 W/(m*K) and 8.1 W/(m*K) respectively, conforming to ASTM E 1461 test standard.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,brk,Type I,5mm/min | 550 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 0.6 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 120300 | kgf/cm² | ASTM D 638 |
| Flexural Stress,brk,1.3mm/min,50mm span | 830 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 119300 | kgf/cm² | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 8 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 1 | cm-kgf/cm | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT,1.82 MPa,6.4mm,unannealed | 180 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 2.15E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 3.54E-05 | 1/℃ | ASTM E 831 |
| CTE,40℃ to 120℃,flow | 2.71E-05 | 1/℃ | ASTM E 831 |
| CTE,40℃ to 120℃,xflow | 5.83E-05 | 1/℃ | ASTM E 831 |
| Specific Heat | 1.39 | J/g-℃ | ASTM C 351 |
| Thermal Conductivity | 2.3 | W/m-℃ | ASTM E 1530 |
| Ball Pressure Test,125℃ +/- 2℃ | 0 | - | IEC 60695-10-2 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.52 | g/cm³ | ASTM D 792 |
| Mold Shrinkage,flow,24 hrs(5) | 0.5 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.45 | % | ASTM D 955 |
| Melt Flow Rate,285ºC/6.7 kgf | 15.3 | g/10 min | ASTM D 1238 |
| Water Absorption,23℃/24hrs | 0.39 | % | SABIC Method |
| Moisture Absorption(23℃ / 50% RH) | 0.06 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 |
| Dielectric Strength,in oil,1.0mm | 14.1 | kV/mm | ASTM D 149 |
| Relative Permittivity,50/60 Hz | 7.27 | - | ASTM D 150 |
| Relative Permittivity,1 MHz | 4.8 | - | ASTM D 150 |
| Dissipation Factor,50/60 Hz | 0.083 | - | ASTM D 150 |
| Dissipation Factor,1 MHz | 0.043 | - | ASTM D 150 |
| Hot Wire Ignition{PLC) | 0 | PLC Code | UL 746A |
| High Ampere Arc Ign,surface{PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index | 575 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized,94V-0 Flame Class Rating(3) | 1.2 | mm | UL 94 |
| Glow Wire Ignitability Temperature,1.0mm | 825 | ℃ | IEC 60695-2-13 |
| Source GMD,last updated:2011/05/09 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80-90 | ℃ |
| Drying Time | 3-4 | hrs |
| Maximum Moisture Content | 0.01 | % |
| Melt Temperature | 250-280 | ℃ |
| Nozzle Temperature | 250-280 | ℃ |
| Front-Zone 3 Temperature | 250-280 | ℃ |
| Middle-Zone 2 Temperature | 240-280 | ℃ |
| Rear-Zone 1 Temperature | 230-270 | ℃ |
| Mold Temperature | 80-100 | ℃ |
| Back Pressure | 3-9 | MPa |
| Screw Speed | 30-150 | rpm |
| Source GMD,last updated:2011/05/09 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.m-PPE EHM1000 9905M 炭纤充填,导电级