- 产 品：PA6 PX08321 导热尼龙6化合物
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP* Konduit* Compound
LNP Konduit Resin All Series
LNP* Konduit* composite compounds are 10 to 50 times more thermally conductive than conventional unfilled thermoplastics. Konduit composite compounds can conduct heat away from devices into a heat sink or the surrounding air. LNP* specialty compound offerings are available in a broad portfolio of standard and engineering materials
LNP™ Konduit™ Compound PA6 PX08321 塑料物性
Also known as:LNP™Konduit™Compound PX08321
Product reorder name:PX08321
Thermally conductive mineral filled PA6 compound, with through-plane and in-plane thermal conductivity of 2.6 W/(m*K) and 10 W/(m*K) respectively, conforming to ASTM E 1461 test standard.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,brk,Type I,5mm/min | 710 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 0.8 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 140900 | kgf/cm² | ASTM D 638 |
| Flexural Stress,brk,1.3mm/min,50mm span | 1060 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 144700 | kgf/cm² | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 16 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 2 | cm-kgf/cm | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT,1.82 MPa,3.2mm,unannealed | 192 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 1.63E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 2.82E-05 | 1/℃ | ASTM E 831 |
| CTE,40℃ to 120℃,flow | 3.63E-05 | 1/℃ | ASTM E 831 |
| CTE,40℃ to 120℃,xflow | 5.56E-05 | 1/℃ | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.61 | g/cm³ | ASTM D 792 |
| Mold Shrinkage,flow,24 hrs(5) | 0.46 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.39 | % | ASTM D 955 |
| Melt Flow Rate,285ºC/6.7 kgf | 12.2 | g/10 min | ASTM D 1238 |
| Water Absorption,23℃/24hrs | 0.34 | % | SABIC Method |
| Moisture Absorption(23℃/50% RH) | 0.06 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Dielectric Strength,in oil,1.0mm | 14.7 | kV/mm | ASTM D 149 |
| Relative Permittivity,50/60 Hz | 6.2 | - | ASTM D 150 |
| Relative Permittivity,1 MHz | 4.1 | - | ASTM D 150 |
| Dissipation Factor,50/60 Hz | 0.076 | - | ASTM D 150 |
| Dissipation Factor,1 MHz | 0.044 | - | ASTM D 150 |
| Hot Wire Ignition{PLC) | 2 | PLC Code | UL 746A |
| High Ampere Arc Ign,surface{PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized,94HB Flame Class Rating(3) | 1 | mm | UL 94 |
| Glow Wire Ignitability Temperature,1.0mm | 825 | ℃ | IEC 60695-2-13 |
| Source GMD,last updated:2011/05/09 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80-90 | ℃ |
| Drying Time | 3-4 | hrs |
| Melt Temperature | 270-300 | ℃ |
| Nozzle Temperature | 270-300 | ℃ |
| Front-Zone 3 Temperature | 270-300 | ℃ |
| Middle-Zone 2 Temperature | 270-300 | ℃ |
| Rear-Zone 1 Temperature | 260-290 | ℃ |
| Mold Temperature | 80-100 | ℃ |
| Back Pressure | 3-9 | MPa |
| Screw Speed | 30-150 | rpm |
| Source GMD,last updated:2011/05/09 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.PPE GTX679 改善了耐冲击和伸长率,导电级
关健字：【LNP™ Konduit™ Compound PA6 PX08321】