DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® PLS95G50DH2 BK261 is a high flow 50% glass reinforced PA nylon resin using SHIELD Technology, only from DuPont providing exceptional Heat Resistance & High stiffness for automotive under hood applications like charge air cooler caps.
zytel®PLS95G50DH2 BK261是一个高流动的50%玻璃纤维增强尼龙树脂,采用盾构技术,只能从杜邦提供特殊的耐热性和高硬度的应用如汽车罩下增压空气冷却器盖。
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
PA-GF50
>PA-GF50<
|
||
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Flexural Strength
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
247(35.8)
2.6
16900(2450)
15700(2276)
374(54.2)
18
16
80
95
|
175(23.4)
5.0
12300(1783.5)
85
90
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
|
ISO 75-1/-2
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
263(505)
254(489)
265(509)
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Thermal
CLTE, Parallel
23-55℃(73-130℉)
CLTE, Normal
23-55℃(73-130℉)
|
ISO 11359-1/-2
ISO 11359-1/-2
|
E-4/C(E-4/F)
E-4/C(E-4/F)
|
0.1(0.05)
0.85(0.47)
|
|
Other
Density
Water Absorption
Equilibrium 50%RH
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1590(1.59)
1.3
0.6
0.3
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
280-300(535-572)
290(555)
70-120(160-250)
100(210)
2-4
80(175)
<0.2
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23℃ unless otherwise stated.
The above data are preliminary and are subject to change as additional data are developed on subsequent lots.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2010