联系我们
塑胶原料报价
- 产 品：PA12 SX90398 包含不锈钢.导电尼龙12树脂
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP STAT-KON* POLYAMIDES COMPOUND
TOUGH, TAILORED ELECTRICAL PROPERTIES
Polyamide-based LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.
LNP™ STAT-KON™ Compound PA12 SX90398 塑料数据物性表
Also known as:LNP™ Stat-kon™ Compound PDX-S-90398
Product reorder name:SX90398
LNP STAT-KON* SX90398 is a compound based on Nylon 12 resin containing Stainless Steel. Added features of this material include: Electrically Conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yield | 440 | kgf/cm² | ASTM D 638 |
| Tensile Stress,break | 360 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yield | 5.3 | % | ASTM D 638 |
| Tensile Strain,break | 117.2 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 19400 | kgf/cm² | ASTM D 638 |
| Flexural Stress | 630 | kgf/cm² | ASTM D 790 |
| Flexural Modulus | 18100 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield | 38 | MPa | ISO 527 |
| Tensile Stress,break | 35 | MPa | ISO 527 |
| Tensile Modulus,1mm/min | 1440 | MPa | ISO 527 |
| Flexural Stress | 50 | MPa | ISO 178 |
| Flexural Modulus | 1760 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | NB | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 7 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Energy @ peak,23℃ | 99 | cm-kgf | ASTM D 3763 |
| Multiaxial Impact | 212 | cm-kgf | ISO 6603 |
| Izod Impact,unnotched 80*10*4 +23℃ | 85 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 113 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 67 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 1.03E-04 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 9.93E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 1.04E-04 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 9.94E-05 | 1/℃ | ISO 11359-2 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 104 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 73 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.102 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.2 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 1.1 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 1.7 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 1.12 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 1.7 | % | ISO 294 |
| Density | 1.09 | g/cm³ | ISO 1183 |
| Moisture Absorption(23℃/50% RH) | 0.3 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+02-1.E+06 | Ohm | ASTM D 257 |
| Source GMD,last updated:2004/10/01 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4-6 | hrs |
| Maximum Moisture Content | 0.12-0.2 | % |
| Melt Temperature | 205 | ℃ |
| Front-Zone 3 Temperature | 230-245 | ℃ |
| Middle-Zone 2 Temperature | 205-215 | ℃ |
| Rear-Zone 1 Temperature | 180-195 | ℃ |
| Mold Temperature | 80-110 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2004/10/01 | ||