- 产 品：PA12 SX93441D 专有填料复合尼龙12,内部润滑
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
NP* Lubricomp* Compound
LNP Lubricomp Resin All Series
LNP* Lubricomp* compounds provide improved wear resistance and lower friction by combining engineering resins with internal lubricants. Lubricomp compounds, which can also be stiffened with glass or other fiber, can help extend product life and reduce or eliminate squeaks and other noise from moving parts. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™ LUBRICOMP™ Compound PA12 SX93441D 塑料数据
Also known as:LNP™ Lubricomp™ Compound PDX-S-93441
Product reorder name:SX93441D
LNP* Lubricomp* SX93441D is a compound based on Nylon 12 containing Proprietary Fillers. Characteristics of this grade are: Internally Lubricated.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5mm/min | 940 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5mm/min | 870 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5mm/min | 4.9 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 6.1 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 55100 | kgf/cm² | ASTM D 638 |
| Flexural Modulus,1.3mm/min,50mm span | 45600 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,5mm/min | 92 | MPa | ISO 527 |
| Tensile Stress,break,5mm/min | 91 | MPa | ISO 527 |
| Tensile Strain,yield,5mm/min | 4.9 | % | ISO 527 |
| Tensile Strain,break,5mm/min | 6.3 | % | ISO 527 |
| Tensile Modulus,1mm/min | 5410 | MPa | ISO 527 |
| Flexural Stress | 136 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 4720 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 88 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 12 | cm-kgf/cm | ASTM D 256 |
| Multiaxial Impact | 37 | cm-kgf | ISO 6603 |
| Instrumented Impact Total Energy,23℃ | 163 | cm-kgf | ASTM D 3763 |
| Izod Impact,unnotched 80*10*4 +23℃ | 58 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 10 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 175 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 161 | ℃ | ASTM D 648 |
| CTE,-30℃ to 30℃,flow | 4.00E+01 | 1/℃ | ASTM D 696 |
| CTE,-30℃ to 30℃,xflow | 1.35E+03 | 1/℃ | ASTM D 696 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 170 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 146 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Density | 1.19 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.15 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 0.3-0.6 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.9-2 | % | ASTM D 955 |
| Wear Factor Washer | 51 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Wear Factor Ring | 7 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.48 | - | ASTM D 3702 Modified |
| Static COF | 0.47 | - | ASTM D 3702 Modified |
| Moisture Absorption(23℃/50% RH) | 0.2 | % | ISO 62 |
| Source GMD,last updated:2011/04/11 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.12-0.2 | % |
| Melt Temperature | 225-240 | ℃ |
| Front-Zone 3 Temperature | 225-240 | ℃ |
| Middle-Zone 2 Temperature | 220-230 | ℃ |
| Rear-Zone 1 Temperature | 215-225 | ℃ |
| Mold Temperature | 70-80 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2011/04/11 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【LNP™ LUBRICOMP™ Compound PA12 SX93441D】