ZENITE® ZE55201 BK010 BLACK
ZENITE ZE55201 | LCP | Mineral / Glass Reinforced
Description
Zenite® ZE55201 is a 50% mineral/glass fiber reinforced liquid crystal polymer for injection molding. and It is specifically suitable for applications requiring ultra flatness.
Other Processing
Injection Molding
Melt Temperature Range = 330-350℃
Melt Temperature Optimum = 335℃
Mold Temperature Optimum = 80℃
Mold Temperature Range = 40-150℃
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
Phys |
Density |
1850 |
kg/m³ |
ISO 1183 |
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
Tensile modulus (1mm/min) |
15800 |
MPa |
ISO 527-2/1A |
Tensile stress at break (5mm/min) |
88 |
MPa |
ISO 527-2/1A |
Tensile strain at break (5mm/min) |
1.4 |
% |
ISO 527-2/1A |
Flexural modulus (23℃) |
12500 |
MPa |
ISO 178 |
Flexural strength (23℃) |
165 |
MPa |
ISO 178 |
Compressive stress @ 1% strain |
21.3 |
MPa |
ISO 604 |
Charpy notched impact strength @ 23℃ |
3.6 |
kJ/m² |
ISO 179/1eA |
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
Melting temperature (10℃/min) |
335 |
℃ |
ISO 11357-1,-2,-3 |
DTUL @ 1.8 MPa |
290 |
℃ |
ISO 75-1/-2 |
DTUL @ 0.45 MPa |
300 |
℃ |
ISO 75-1/-2 |
Coeff.of linear therm. expansion (parallel) |
0.15 |
E-4/℃ |
ISO 11359-2 |
Coeff.of linear therm. expansion (normal) |
0.27 |
E-4/℃ |
ISO 11359-2 |
Limiting oxygen index (LOI) |
41 |
% |
ISO 4589 |
Flammability @1.6mm nom. thickn. |
V-0 |
class |
UL94 |
thickness tested (1.6) |
1.5 |
mm |
UL94 |
UL recognition (1.6) |
UL |
- |
UL94 |
Flammability at thickness h |
V-0 |
class |
UL94 |
thickness tested (h) |
0.8 |
mm |
UL94 |
UL recognition (h) |
UL |
- |
UL94 |
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
Relative permittivity - 1 MHz |
4 |
- |
IEC 60250 |
Dissipation factor - 100 Hz |
310 |
E-4 |
IEC 60250 |
Dissipation factor - 1 MHz |
310 |
E-4 |
IEC 60250 |
Volume resistivity |
>1E13 |
Ohm*m |
IEC 60093 |
Surface resistivity |
>1E15 |
Ohm |
IEC 60093 |
Electric strength |
37 |
kV/mm |
IEC 60243-1 |
Comparative tracking index CTI |
175 |
- |
IEC 60112 |
Rheo |
Rheological Calculation properties |
Value |
Unit |
Test Standard |
Density of melt |
1620 |
kg/m³ |
Internal |
Thermal conductivity of melt |
0.4 |
W/(m K) |
Internal |
Specific heat capacity of melt |
1500 |
J/(kg K) |
Internal |
Ejection temperature |
270 |
℃ |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.01%
Drying time (h):3
Drying temperature (℃):150--