联系我们
- 产 品：LCP S135 含35%玻璃纤维增强,除气作用低至无
- 产 地：泰科纳
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
VECTRA® S135 BK010P BLACK
VECTRA® S135 BK010P BLACK (FDA)
VECTRA® S135 VF2001 NATURAL
VECTRA® S135 VF2001 NATURAL (FDA)
VECTRA S135 | LCP | Glass Reinforced
Description
35% glass reinforced Vectra grade with very low outgassing, very high heat deflection temperature (335℃) and stiffness. Typical applications are lampsockets, lensholders for beamers, electrical and electronic parts like connectors, relays, switches, coil bobbins and also under the hood applications.
Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant
UL-Listing V-0 in natural at 0.28mm thickness per UL 94 flame testing.
Relative-Temperature-Index (RTI) according to UL 746B: electrical 130℃, mechanical 130℃.
UL = Underwriters Laboratories (USA)
Other Processing
Injection Molding
A three-zone screw evenly divided into feed, compression, and metering zones is preferred. A higher percentage of feed flights may be needed for smaller machines: ½ feed, ¼ compression, ¼ metering.
Vectra LCPs are shear thinning, their melt viscosity decreases quickly as shear rate increases. For parts that are difficult to fill, the molder can increase the injection velocity to improve melt flow.
| ISO Data | Physical properties | Value | Unit | Test Standard |
| Phys | Density | 1670 | kg/m³ | ISO 1183 |
| Mold shrinkage - parallel | 0.4 | % | ISO 294-4 | |
| Mold shrinkage - normal | 0.6 | % | ISO 294-4 | |
| Mech | Mechanical properties | Value | Unit | Test Standard |
| Tensile stress at break (5mm/min) | 140 | MPa | ISO 527-2/1A | |
| Tensile strain at break (5mm/min) | 1.3 | % | ISO 527-2/1A | |
| Flexural modulus (23℃) | 14500 | MPa | ISO 178 | |
| Flexural strength (23℃) | 230 | MPa | ISO 178 | |
| Flexural strain @ break | 2 | % | ISO 178 | |
| Charpy notched impact strength @ 23℃ | 12 | kJ/m² | ISO 179/1eA | |
| Unnotched impact str (Izod) @ 23℃ | 14 | kJ/m² | ISO 180/1U | |
| Notched impact strength (Izod) @ 23℃ | 12 | kJ/m² | ISO 180/1A | |
| Therm | Thermal properties | Value | Unit | Test Standard |
| Melting temperature (10℃/min) | 350 | ℃ | ISO 11357-1,-2,-3 | |
| DTUL @ 1.8 MPa | 340 | ℃ | ISO 75-1/-2 | |
| DTUL @ 8.0 MPa | 267 | ℃ | ISO 75-1/-2 | |
| Coeff.of linear therm. expansion (parallel) | 0.01 | E-4/℃ | ISO 11359-2 | |
| Coeff.of linear therm. expansion (normal) | 0.23 | E-4/℃ | ISO 11359-2 | |
| Flammability at thickness h | V-0 | class | UL94 | |
| Elec | Electrical properties | Value | Unit | Test Standard |
| Relative permittivity - 1 MHz | 3.5 | - | IEC 60250 | |
| Dissipation factor - 1 MHz | 90 | E-4 | IEC 60250 | |
| Volume resistivity | 1.00E+15 | Ohm*m | IEC 60093 | |
| Surface resistivity | 1.00E+17 | Ohm | IEC 60093 | |
| Electric strength | 37 | kV/mm | IEC 60243-1 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.01%
VECTRA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 40℃. The time between drying and processing should be as short as possible.
For subsequent storage of the material in the dryer until processed the temperature does not need to be lowered for grades A, B, C, D and V (<= 24 h).
Drying time (h):6
Drying temperature (℃):150-170