- 产 品：LCP E135i 含35%的玻璃纤维,熔接线强度更高
- 产 地：泰科纳
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
VECTRA® E135I VC3052 GRAY
VECTRA® E135I VD3005 BLACK
VECTRA® E135I VF3001 NATURAL
VECTRA E135i | LCP | Glass Reinforced
Description
35% glass fiber filled /Higher weldline strength.
Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant.
FDA compliant.
UL-Listing V-0 in all colors at .15mm thickness per UL 94 flame testing.
UL = Underwriters Laboratories (USA)
| ISO Data | Physical properties | Value | Unit | Test Standard |
| Phys | Density | 1670 | kg/m³ | ISO 1183 |
| Mold shrinkage - parallel | 0 | % | ISO 294-4 | |
| Mold shrinkage - normal | 0.29 | % | ISO 294-4 | |
| Water absorption (23℃-sat) | 0.07 | % | ISO 62 | |
| Mech | Mechanical properties | Value | Unit | Test Standard |
| Tensile modulus (1mm/min) | 16000 | MPa | ISO 527-2/1A | |
| Tensile stress at break (5mm/min) | 150 | MPa | ISO 527-2/1A | |
| Tensile strain at break (5mm/min) | 1.5 | % | ISO 527-2/1A | |
| Flexural modulus (23℃) | 17000 | MPa | ISO 178 | |
| Flexural strength (23℃) | 225 | MPa | ISO 178 | |
| Flexural strain @ break | 2.1 | % | ISO 178 | |
| Compressive stress @ 1% strain | 100 | MPa | ISO 604 | |
| Charpy impact strength @ 23℃ | 40 | kJ/m² | ISO 179/1eU | |
| Charpy notched impact strength @ 23℃ | 27 | kJ/m² | ISO 179/1eA | |
| Unnotched impact str (Izod) @ 23℃ | 40 | kJ/m² | ISO 180/1U | |
| Notched impact strength (Izod) @ 23℃ | 30 | kJ/m² | ISO 180/1A | |
| Compressive modulus | 13500 | MPa | ISO 604 | |
| Rockwell hardness | 62 | M-Scale | ISO 2039-2 | |
| Therm | Thermal properties | Value | Unit | Test Standard |
| Melting temperature (10℃/min) | 335 | ℃ | ISO 11357-1,-2,-3 | |
| DTUL @ 1.8 MPa | 275 | ℃ | ISO 75-1/-2 | |
| Vicat softening temperature B50 (50℃/h 50N) | 200 | ℃ | ISO 306 | |
| Coeff.of linear therm. expansion (parallel) | 0.05 | E-4/℃ | ISO 11359-2 | |
| Coeff.of linear therm. expansion (normal) | 0.59 | E-4/℃ | ISO 11359-2 | |
| Elec | Electrical properties | Value | Unit | Test Standard |
| Relative permittivity - 1 MHz | 4.1 | - | IEC 60250 | |
| Dissipation factor - 1 MHz | 30 | E-4 | IEC 60250 | |
| Volume resistivity | 1.00E+14 | Ohm*m | IEC 60093 | |
| Surface resistivity | 1.00E+15 | Ohm | IEC 60093 | |
| Electric strength | 28 | kV/mm | IEC 60243-1 | |
| Comparative tracking index CTI | 175 | - | IEC 60112 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.01%
VECTRA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 40℃. The time between drying and processing should be as short as possible.
Drying time (h):4
Drying temperature (℃):150 - 150