ZENITE® 5244L BK010 BLACK
ZENITE® 5244L WT010 WHITE
ZENITE 5244L | LCP | Mineral / Glass Reinforced
Description
Zenite 5244L is a 40% glass/mineral reinforced LCP resin with improved toughness.
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
Phys |
Density |
1710 |
kg/m³ |
ISO 1183 |
Mold shrinkage - parallel |
0.1 |
% |
ISO 294-4 |
Mold shrinkage - normal |
0.4 |
% |
ISO 294-4 |
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
Tensile modulus (1mm/min) |
14000 |
MPa |
ISO 527-2/1A |
Tensile stress at break (5mm/min) |
131 |
MPa |
ISO 527-2/1A |
Tensile strain at break (5mm/min) |
1.66 |
% |
ISO 527-2/1A |
Flexural modulus (23℃) |
13100 |
MPa |
ISO 178 |
Flexural strength (23℃) |
198 |
MPa |
ISO 178 |
Charpy impact strength @ 23℃ |
27 |
kJ/m² |
ISO 179/1eU |
Charpy notched impact strength @ 23℃ |
16.6 |
kJ/m² |
ISO 179/1eA |
Unnotched impact str (Izod) @ 23℃ |
28 |
kJ/m² |
ISO 180/1U |
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
Melting temperature (10℃/min) |
318 |
℃ |
ISO 11357-1,-2,-3 |
DTUL @ 1.8 MPa |
285 |
℃ |
ISO 75-1/-2 |
Coeff.of linear therm. expansion (parallel) |
0.06 |
E-4/℃ |
ISO 11359-2 |
Coeff.of linear therm. expansion (normal) |
0.48 |
E-4/℃ |
ISO 11359-2 |
Flammability @1.6mm nom. thickn. |
V-0 |
class |
UL94 |
thickness tested (1.6) |
1.5 |
mm |
UL94 |
UL recognition (1.6) |
UL |
- |
UL94 |
Flammability at thickness h |
V-0 |
class |
UL94 |
thickness tested (h) |
0.8 |
mm |
UL94 |
UL recognition (h) |
UL |
- |
UL94 |
Processing
Pre Drying
Drying time (h):3
Drying temperature (℃):150-150