快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：LCP 5145L 含45%玻璃纤维增强,改善了韧性
- 产 地：泰科纳
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
ZENITE® 5145L BK010 BLACK
ZENITE® 5145L BK010S BLACK
ZENITE® 5145L GY001A GRAY
ZENITE® 5145L WT010 WHITE
ZENITE 5145L | LCP | Glass Reinforced
Description
Zenite® 5145L is a 45% glass fiber reinforced and toughened liquid crystal polymer for injection molding. It has improved toughness.
Other Processing
Injection Molding
Melt Temperature Optimum = 335℃
Melt Temperature Range = 325-345℃
Mold Temperature Optimum = 80℃
Mold Temperature Range = 40-150℃
| ISO Data | Physical properties | Value | Unit | Test Standard |
| Phys | Density | 1750 | kg/m³ | ISO 1183 |
| Mold shrinkage - parallel | 0.09 | % | ISO 294-4 | |
| Mold shrinkage - normal | 0.5 | % | ISO 294-4 | |
| Mech | Mechanical properties | Value | Unit | Test Standard |
| Tensile modulus (1mm/min) | 15000 | MPa | ISO 527-2/1A | |
| Tensile stress at break (5mm/min) | 115 | MPa | ISO 527-2/1A | |
| Tensile strain at break (5mm/min) | 3.1 | % | ISO 527-2/1A | |
| Flexural modulus (23℃) | 11000 | MPa | ISO 178 | |
| Flexural strength (23℃) | 190 | MPa | ISO 178 | |
| Compressive strength | 71 | MPa | ISO 604 | |
| Compressive stress @ 1% strain | 21.3 | MPa | ISO 604 | |
| Therm | Thermal properties | Value | Unit | Test Standard |
| Melting temperature (10℃/min) | 319 | ℃ | ISO 11357-1,-2,-3 | |
| DTUL @ 1.8 MPa | 290 | ℃ | ISO 75-1/-2 | |
| Coeff.of linear therm. expansion (parallel) | 0.07 | E-4/℃ | ISO 11359-2 | |
| Coeff.of linear therm. expansion (normal) | 0.6 | E-4/℃ | ISO 11359-2 | |
| Limiting oxygen index (LOI) | 33 | % | ISO 4589 | |
| Flammability @1.6mm nom. thickn. | V-0 | class | UL94 | |
| thickness tested (1.6) | 1.5 | mm | UL94 | |
| UL recognition (1.6) | UL | - | UL94 | |
| Flammability at thickness h | V-0 | class | UL94 | |
| thickness tested (h) | 0.8 | mm | UL94 | |
| UL recognition (h) | UL | - | UL94 | |
| Elec | Electrical properties | Value | Unit | Test Standard |
| Relative permittivity - 1 MHz | 3.9 | - | IEC 60250 | |
| Dissipation factor - 1 MHz | 180 | E-4 | IEC 60250 | |
| Volume resistivity | 1.00E+13 | Ohm*m | IEC 60093 | |
| Surface resistivity | 1.00E+15 | Ohm | IEC 60093 | |
| Electric strength | 45 | kV/mm | IEC 60243-1 | |
| Comparative tracking index CTI | 175 | - | IEC 60112 | |
| Rheo | Rheological Calculation properties | Value | Unit | Test Standard |
| Density of melt | 1480 | kg/m³ | Internal | |
| Thermal conductivity of melt | 0.35 | W/(m K) | Internal | |
| Specific heat capacity of melt | 1500 | J/(kg K) | Internal | |
| Ejection temperature | 265 | ℃ | Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.01%
Drying time (h)：3
Drying temperature (℃)：150-150