LNP STAT-KON* STYRENICS COMPOUND
TAILOR THE ELECTRICAL ACTIVITY OF STYRENES
Styrenic LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.
LNP™ STAT-KON™ Compound COC 9X06519 塑料物性表
Also known as:LNP™ Stat-kon™ Compound COC-C-1006 CCS
Product reorder name:9X06519
LNP STAT-KON* 9X06519 is a compound based on Cyclic Olefinic Copolymer resin containing Carbon Fiber. Added features of this material include: Clean Compounding System.
MECHANICAL | Value | Unit | Standard |
Tensile Stress,break | 760 | kgf/cm² | ASTM D 638 |
Tensile Strain,break | 0.5 | % | ASTM D 638 |
Tensile Modulus,50mm/min | 163600 | kgf/cm² | ASTM D 638 |
Flexural Stress | 1610 | kgf/cm² | ASTM D 790 |
Flexural Modulus | 170100 | kgf/cm² | ASTM D 790 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 12 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 3 | cm-kgf/cm | ASTM D 256 |
THERMAL | Value | Unit | Standard |
HDT,1.82 MPa,3.2mm,unannealed | 150 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 2.80E-06 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,xflow | 1.26E-05 | 1/℃ | ASTM E 831 |
PHYSICAL | Value | Unit | Standard |
Density | 1.17 | g/cm³ | ASTM D 792 |
ELECTRICAL | Value | Unit | Standard |
Surface Resistivity | 1.E+01-1.E+05 | Ohm | ASTM D 257 |
Source GMD,last updated:2005/02/03 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 80 | ℃ |
Drying Time | 4 | hrs |
Melt Temperature | 260-315 | ℃ |
Front-Zone 3 Temperature | 300-310 | ℃ |
Middle-Zone 2 Temperature | 275-290 | ℃ |
Rear-Zone 1 Temperature | 255-265 | ℃ |
Mold Temperature | 80-110 | ℃ |
Back Pressure | 0.2-0.3 | MPa |
Screw Speed | 30-60 | rpm |
Source GMD,last updated:2005/02/03 |